Ferritic nitrocarburizing or FNC, also known by the proprietary names Tenifer, Tufftride and Melonite as well as ARCOR, is a range of proprietary case hardening processes that diffuse nitrogen and carbon into ferrous metals at sub-critical temperatures during a salt bath. Other methods of ferric nitrocarburizing include gaseous processes such as Nitrotec and ion (plasma) ones. The processing temperature ranges from to , but usually occurs at . At this temperature steels and other ferrous alloys remain in the ferritic phase region. This allows for better control of the dimensional stability that would not be present in case hardening processes that occur when the alloy is transitioned into the austenitic phase. There are four main classes of ferritic nitrocarburizing: gaseous, salt bath, ion or plasma, and fluidized-bed.
The process is used to improve three main surface integrity aspects including scuffing resistance, fatigue properties, and corrosion resistance. It has the added advantage of inducing little shape distortion during the hardening process. This is because of the low processing temperature, which reduces thermal shocks and avoids phase transitions in steel.
History
The first ferritic nitrocarburizing methods were done at low temperatures, around , in a liquid salt bath. The first company to successfully commercialize the process was the Imperial Chemical Industries in Great Britain. ICI called their process "the cassel" due to the plant where it was developed or "Sulfinuz" treatment because it had sulfur in the salt bath. While the process was very successful with high-speed spindles and cutting tools, there were issues with cleaning the solution off because it was not very water soluble.
Because of the cleaning issues, Lucas Industries began experimenting with gaseous forms of ferritic nitrocarburizing in the late 1950s. The company applied for a patent in 1961. It produced a similar surface finish as the Sulfinuz process with the exception of the formation of sulfides. The atmosphere consisted of ammonia, hydrocarbon gases, and a small amount of other carbon-containing gases.
This spurred the development of a more environmentally friendly salt bath process by the German company Degussa after acquiring ICI patents. Their process is the widely known as the Tufftride or Tenifer process. Following this, the ion nitriding process was invented in the early 1980s. This process had faster cycle times, required less cleaning and preparation, formed deeper cases, and allowed for better control of the process.
Processes
Despite the naming, the process is a modified form of nitriding and not carburizing. The shared attribute of this class of this process is the introduction of nitrogen and carbon in the ferritic state of the material. The processes are divided into four main classes: gaseous, salt bath, ion or plasma, or fluidized-bed. The trade name and patented processes may vary slightly from the general description, but they are all a form of ferritic nitrocarburizing.
Salt bath ferritic nitrocarburizing
Salt bath ferritic nitrocarburizing is also known as liquid ferritic nitrocarburizing or liquid nitrocarburizing and is also known by the trademarked names Tufftride and Tenifer.
The simplest form of this process is encompassed by the trademarked Melonite process, also known as Meli 1. It is most commonly used on steels, sintered irons, and cast irons to lower friction and improve wear and corrosion resistance.
The process uses a salt bath of alkali cyanate. This is contained in a steel pot that has an aeration system. The cyanate thermally reacts with the surface of the workpiece to form an alkali carbonate. The bath is then treated to convert the carbonate back to a cyanate. The surface formed from the reaction has a compound layer and a diffusion layer. The compound layer consists of iron, nitrogen, and oxygen is abrasion resistant and is stable at elevated temperatures. The diffusion layer contains nitrides and carbides. The surface hardness ranges from 800 to 1500 HV depending on the steel grade. This also inversely affects the depth of the case; i.e. a high carbon steel will form a hard, but shallow case.
A similar process is the trademarked Nu-Tride process, also known incorrectly as the Kolene process (which is actually the company's name), which includes a preheat and an intermediate quench cycle. The intermediate quench is an oxidizing salt bath at . This quench is held for 5 to 20 minutes before the final quenching to room temperature. This is done to minimize distortion and to destroy any lingering cyanates or cyanides left on the workpiece.