Glass recycling is the processing of waste glass into usable products. Glass that is crushed or imploded and ready to be remelted is called cullet. There are two types of cullet: internal and external. Internal cullet is composed of defective products detected and rejected by a quality control process during the industrial process of glass manufacturing, transition phases of product changes (such as thickness and color changes) and production offcuts. External cullet is waste glass that has been collected or reprocessed with the purpose of recycling. External cullet (which can be pre- or post-consumer) is classified as waste. The word "cullet", when used in the context of end-of-waste, will always refer to external cullet.
To be recycled, glass waste needs to be purified and cleaned of contamination. Then, depending on the end use and local processing capabilities, it might also have to be separated into different sizes and colours. Many recyclers collect different colors of glass separately since glass retains its color after recycling. The most common colours used for consumer containers are clear (flint) glass, green glass, and brown (amber) glass. Glass is ideal for recycling since none of the material is degraded by normal use.
Many collection points have separate bins for clear (flint), green and brown (amber). Glass re-processors intending to make new glass containers require separation by color, because glass tends to retain its color after recycling. If the recycled glass is not going to be made into more glass, or if the glass re-processor uses newer optical sorting equipment, separation by color at the collection point may not be required. Heat-resistant glass, such as Pyrex or borosilicate glass, must not be part of the glass recycling stream, because even a small piece of such material will alter the viscosity of the fluid in the furnace at remelt.
Processing of external cullet
To be able to use external cullet in production, any contaminants should be removed as much as possible. Typical contaminations are:
Organics: Paper, plastics, caps, rings, PVB foils for flat glass
Inorganics: Stones, ceramics, porcelains
Metals: Ferrous and non-ferrous metals
Heat resistant and lead glass
Manpower or machinery can be used in different stages of purification. Since they melt at higher temperatures than glass, separation of inorganics, the removal of heat resistant glass and lead glass is critical. In the modern recycling facilities, dryer systems and optical sorting machines are used. The input material should be sized and cleaned for the highest efficiency in automatic sorting. More than one free fall or conveyor belt sorter can be used, depending on the requirements of the process. Different colors can be sorted by optical sorting machines.
Recycling into glass containers
Glass bottles and jars are infinitely recyclable. The use of recycled glass in manufacturing conserves raw materials and reduces energy consumption. Because the chemical energy required to melt the raw materials has already been expended, the use of cullet can significantly reduce energy consumption compared with manufacturing new glass from silica (SiO2), soda ash (Na2CO3), and calcium carbonate (CaCO3). Soda lime glass from virgin raw materials theoretically requires approximately 2.671 GJ/tonne compared to 1.886 GJ/tonne to melt 100% glass cullet. As a general rule, every 10% increase in cullet usage results in an energy savings of 2–3% in the melting process, with a theoretical maximum potential of 30% energy saving. Every metric ton (1,000 kg) of waste glass recycled into new items saves of carbon dioxide from being released into the atmosphere during the manufacture of new glass.
Recycling into other products
The use of the recycled glass as aggregate in concrete has become popular, with large-scale research on that application being carried out at Columbia University in New York. Recycled glass greatly enhances the aesthetic appeal of the concrete. Recent research has shown that concrete made with recycled glass aggregates have better long-term strength and better thermal insulation, due to the thermal properties of the glass aggregates. Glass which is not recycled, but crushed, reduces the volume of waste sent to landfill. Waste glass may also be kept out of landfill by using it for roadbed aggregate.