The accompanying illustration (fig. 231) shows an Astatic Galvanometer which may be used in two ways—either to measure strength of current, or to find out a current; in the latter case it would be termed a Galvanoscope. It is a compound needle instrument, and consists of two needles placed in parallel directions with opposite poles above each other in a coil. The wire coil is wound round a bobbin, and the astatic needle is placed therein and suspended freely, as in the illustration, by a cocoon thread. The upper needle moves upon a scale, O O, and the instrument is enclosed in a glass shade. The screw, V, communicates with the upper needle, and fixes it at zero point when ready for use. The wires are fastened to the binding-screws, and the current is then sent. The needle is deflected accordingly, and the number of degrees on the scale can be read off.
The uses of the galvanic current are many. Amongst them Electroplating is perhaps the most generally useful, though Electrotyping is also a very important process in art. A visitor to Birmingham may view the process carried on there by some enterprising firms, who have succeeded wonderfully in producing electro-plate. The principle is very simple and easy to understand, but the greatest care and watchfulness are required on the part of the men employed. The principle, as we have said, is simple, and consists in the fact that if a plate of metal be suspended and attached to the positive pole of a galvanic battery and immersed in a solution of the same metal, the conducting substance hung opposite at the negative pole becomes coated with the metal immersed in the solution.
[Illustration: Fig. 232.—Trough for electro-deposition.]
[Illustration: Fig. 233.—Plates immersed.]
Suppose we take a plate of silver, and immerse it in cyanide of silver dissolved in cyanide of potassium; a coating of silver will be deposited upon the nickel spoon or other article suspended at the other pole. But to make the coating adhere the spoons, forks, etc., are prepared for the bath by cleansing in caustic potash to remove grease, and washed in nitric acid to remove all traces of oxide, then are scoured with sand. Next, a thin coating of mercury is put on by immersion in solution of nitrate of mercury. Finally, they are hung in the bath. A metal rod is hung across the bath (fig. 232), and the plate is immersed. If the rod to which the articles are suspended be attached to the zinc or negative pole, and the plate of silver to the positive pole of the battery, decomposition begins, and the silver begins to attach itself to the suspended objects. If it be desirable to give the plated articles a thick coating, they are retained for a long time in the bath, which is of some non-conducting material. The dull appearance is easily removed by brushing and burnishing, and then the “Electro-plate” is ready for the warehouse. The gilding process is performed in the same manner, a gold plate being substituted for the silver.