Wood drying (also seasoning lumber or wood seasoning) reduces the moisture content of wood before its use. When the drying is done in a kiln, the product is known as kiln-dried timber or lumber, whereas air drying is the more traditional method.
There are two main reasons for drying wood: WoodworkingWhen wood is used as a construction material, whether as a structural support in a building or in woodworking objects, it will absorb or expel moisture until it is in equilibrium with its surroundings. Equilibration (usually drying) causes unequal shrinkage in the wood, and can cause damage to the wood if equilibration occurs too rapidly. The equilibration must be controlled to prevent damage to the wood. Wood burning When wood is burned (firewood), it is usually best to dry it first. Damage from shrinkage is not a problem here, as it may be in the case of drying for woodworking purposes. Moisture affects the burning process, with unburnt hydrocarbons going up the chimney. If a 50% wet log is burnt at high temperature, with good heat extraction from the exhaust gas leading to a 100 °C exhaust temperature, about 5% of the energy of the log is wasted through evaporating and heating the water vapour. With condensers, the efficiency can be further increased; but, for the normal stove, the key to burning wet wood is to burn it very hot, perhaps starting fire with dry wood.
For some purposes, wood is not dried at all, and is used green. Often, wood must be in equilibrium with the air outside, as for construction wood, or the air indoors, as for wooden furniture.
Wood is air-dried or dried in a purpose built oven (kiln). Usually the wood is sawn before drying, but sometimes the log is dried whole.
Case hardening describes lumber or timber that has been dried too rapidly. Wood initially dries from the shell (surface), shrinking the shell and putting the core under compression. When this shell is at a low moisture content it will 'set' and resist shrinkage. The core of the wood is still at a higher moisture content. This core will then begin to dry and shrink. However, any shrinkage is resisted by the already 'set' shell. This leads to reversed stresses; compression stresses on the shell and tension stresses in the core. This results in unrelieved stress called case hardening. Case-hardened [wood] may warp considerably and dangerously when the stress is released by sawing.
Types of wood
Wood is divided, according to its botanical origin, into two kinds: softwoods, from coniferous trees, and hardwoods, from broad-leaved trees. Softwoods are lighter and generally simple in structure, whereas hardwoods are harder and more complex. However, in Australia, softwood generally describes rain forest trees, and hardwood describes Sclerophyll species (Eucalyptus spp).
Softwoods such as pine are typically much lighter and easier to process than hardwoods such as fruit tree wood. The density of softwoods ranges from to , while hardwoods are to . Once dried, both consist of approximately 12% of moisture (Desch and Dinwoodie, 1996). Because of hardwood's denser and more complex structure, its permeability is much less than that of softwood, making it more difficult to dry. Although there are about a hundred times more species of hardwood trees than softwood trees, the ability to be dried and processed faster and more easily makes softwood the main supply of commercial wood nowadays.
Wood–water relationships
When green wood dries, free water from the cell lumina, held by the capillary forces only, is the first to go. Physical properties, such as strength and shrinkage, are generally not affected by the removal of free water. The fibre saturation point (FSP) is defined as the moisture content at which free water should be completely gone, while the cell walls are saturated with bound water. In most types of woods, the fibre saturation point is at 25 to 30% moisture content. Siau (1984) reported that the fibre saturation point The timber of living trees and fresh logs contains a large amount of water which often constitutes over 50% of the wood's weight. Water has a significant influence on wood. Wood continually exchanges moisture or water with its surroundings, although the rate of exchange is strongly affected by the degree to which wood is sealed.