The following points should be observed in the application of the method. Vessels of glass or glazed earthenware should be used for the reduction, while long swords can be put into tall glass cylinders or into wooden troughs, the interior of which must be coated over with paraffin. The soda solution must be kept in a closed glass bottle[129]. It should be diluted with water until the specific gravity, as shown by the hydrometer, is 1·06; the mixture will then contain about 5 per cent. of caustic soda. During the reduction process the mixture frequently assumes a brownish colour as the result of the presence of organic matter associated with the rust. On account of the dissolved zinc which it contains it cannot be used a second time, unless regenerated by boiling with quicklime. The solution is, however, so cheap that this is scarcely worth the trouble.
The objects should be handled with metal tongs, and should not be touched with the hand until they have at least been dipped or rinsed in water, for the soda solution has an injurious effect upon the skin. A basin containing vinegar, dilute hydrochloric or sulphuric acid should always be at hand into which the fingers should be quickly dipped if they have been in contact with the caustic soda. These materials will serve also for cleaning the vessels used in the reduction process.
The zinc strips should be 1/4 to 1/3 inch [1/2 cm. to 1 cm.] in breadth, and should be cut out of a piece of sheet zinc of moderate thickness, but of sufficient pliability.
Any firmly fixed rust may be removed by mechanical means, such as the graver, drill, etc., as has been previously mentioned. If in rinsing a slight layer of oxide appears, although this is rare, it should be brushed off with a steel-wire brush.
If one portion only of a specimen requires reduction (the other portion having, for example, remains of wood attached, and therefore being unsuitable for reduction), that portion only should be wrapped with the zinc and immersed in the solution.
The results obtained by Krefting's preservation-process are quite as surprising as those which are afforded by Blell's method. Figure 29, taken from Appelgren's work, shows the lower portion of a spear-head before and after treatment, by which it became apparent that the whole socket was plated with silver, with two engraved and gilded animal figures. Fig. 34 represents a piece of a sword, on which an inscription was brought to light by the reduction process.