This is all that scientific research has so far been able to tell us of the intimate constitution of porcelain; but as far as it goes, it is evidence in favour of our claim that we are dealing with a definite substance, _sui generis_, and not merely with a casual mixture of certain superior kinds of clay, something, as we have said, between glass and stoneware.
There are certain other elements that enter at times into the composition of porcelain--magnesia, which may have been added to the paste in the form either of steatite or magnesite; and lime, derived either from gypsum or chalk. These additions generally tend to increase the fusibility of the paste, especially when accompanied by an additional dose of silica; but as their presence is not essential we are not concerned with these substances here.
The glazes used for porcelain are as a rule distinguished by their comparative infusibility and by their containing no lead. The composition of these glazes follows more or less that of the paste that they cover, with such modifications, however, as to allow of a somewhat lower fusing-point: as in the case of the paste, there is a harder and more refractory, and a softer and more fusible, type. The harder glazes are composed essentially of felspar, with the addition in most cases of silica, kaolin, and powdered fragments of porcelain. At Sèvres, a natural rock, pegmatite, consisting chiefly of felspar, has been melted to form a glaze without further addition. Of late years, however, the introduction of a milder type of porcelain has necessitated the use of a more fusible glaze, containing a considerable quantity of lime, and it is a glaze of this latter type that has with few exceptions found favour in other districts where porcelain is made.
We have attempted in this chapter to give some idea of the nature of porcelain from a physical and chemical point of view, and in doing so have taken as our type the hard, refractory paste of Europe. When we come to describe the porcelain of the Chinese, we shall notice some important divergences from this type. We say nothing here of the soft-paste porcelains, seeing that so long as we confine ourselves to the question of chemical composition and physical properties, they lie entirely outside our definitions. It is only from the point of view of its history and of its artistic qualities that this group has any claim to the name of porcelain.